Zirconia Fused Alumina Za25 Grain
New Products From This Supplier
Description:
Zirconium corundum is made of high-purity alumina and zirconium material as raw materials. After high temperature smelting at 2250℃, it is formed by special processing technology and Barmac ball milling. It has high quality, extremely hard, compact structure and special crystals, dendritic eutectic structure. According to the content of ZrO2, zirconium corundum can be divided into ZA25 zirconium corundum (ZrO225%) and ZA40 zirconium corundum (ZrO2 40%).
The biggest feature of zirconium corundum that is different from ordinary corundum and silicon carbide is superior self-sharpening, toughness and wear resistance. Used for making grinding wheels, it can significantly improve the life and sharpness of grinding wheels, and for grinding and cutting workpieces with higher hardness, the wear resistance is particularly obvious. Mainly used in the production of heavy-duty grinding wheels, resin grinding wheels, cutting discs, wear-resistant products, high-end abrasive tools, etc., suitable for steel parts, cast iron parts, heat-resistant steel, titanium alloys, nickel alloys, aluminum alloys, tungsten titanium alloys and other materials The grinding force is higher than that of ordinary corundum products.
Characteristic:
- A little less hardness than normal fused alumina
- Higher roughness than alumina without Zirconium.
- 40%ZrO2 Zirconia has better self-sharpening ability， abrasive tools like cutting disc and grinding wheel would be sharper and more durable.
- 25%ZrO2 Zirconia is more Suitable for making heavy duty grinding disc which works good for heat-resistant alloy steel, titanium alloy and austenitic stainless steel.
Application：
- Bonded Abrasives:
Used to produce heavy-duty grinding wheels, barren grinding wheels, rail snagging & grinding wheel, cutting disc, and high-grade resin bonded grinding wheels.
Abrasive Disc for grinding and cutting difficult to grind materials.
Raw material for high-end production of cutting discs, grinding discs, polishing wheels, etc.
- Coated Abrasives:
Used to produce coated abrasives, such as sandpaper, abrasive belts, flexible polishing wheels, etc., to improve polishing accuracy and work efficiency.
- Used to produce wear-resistant hammers, wear-resistant rollers and other wear-resistant products.
- Abrasive sandblasting and surface treatment, suitable for marble, super hard steel and other materials.
- Used for high-level refractory materials to make zirconia refractory bricks, etc.
|
Chemical composition |
||
|
Item |
ZA25 |
ZA40 |
|
AL2O3 |
70-72% |
55-57% |
|
ZrO2 |
24-30% |
35-44% |
|
TiO2 |
Max 1.0% |
Max 0.8% |
|
Fe2O3 |
Max 0.3% |
Max 0.25% |
|
SiO2 |
Max 0.8% |
Max 0.6% |
|
Typical physical properties |
||
|
Item |
ZA25 |
ZA40 |
|
Specific Gravity |
4.30g/cm3 |
4.60g/cm3 |
|
Bulk density(LPD) |
1.90-2.30g/cm3 |
2.15-2.45g/cm3 |
|
Knoop hardness |
1600 |
1450 |
|
Melting Point |
1950℃ |
1900℃ |
|
Particle shape |
Monoclinical tetragonal |
|
|
Chemical property |
Amphoteric |
|
|
Reaction with acid and alkali |
NO |
|
|
Reaction with carbon |
Forming carbide since 1650 ℃ |
|
|
Crystal Size |
≤30 μm |
|
|
Maximum service temperature |
1600 ℃ |
|
|
Color |
Gray |
|
|
Specific heat capacity(cal/g.C) |
0.2205(50-500℃) |
|
|
Heat conductivity |
0.2718 cal/cm2.sec.℃ |
|
|
Linear expansivity(X10-6) |
6.82(100-700℃) |
|
Available sizes：
|
F-Grit（For Bonded Abrasives with high LPD） |
F6 F8 F10 F12 F14 F16 F20 F22 F24 F30 F36 F40 F46 F54 F60 F70 F80 F90 F100 F120 F150 F180 F220 |
|
F-Grit（For sandblasting） |
F6 F8 F10 F12 F14 F16 F20 F22 F24 F30 F36 F40 F46 F54 F60 F70 F80 F90 F100 F120 F150 F180 F220 |
|
P-Grit（For Coated Abrasives） |
40# 50# 60# 80# 100# 120# 150# 180# 220# |
|
Section Sand and Fine Powder（For Refractory） |
0-0.5mm,0-1mm,1-3mm,3-5mm,5-8mm,100#-0,200#-0,320#-0 |
|
Micro-Powder（For Lapping and Polishing） |
(JIS Standard) JIS240#,JIS280#,JIS320#,JIS360#,JIS400,JIS500#,JIS600#,JIS800#,JIS1000#,JIS1200#,JIS1500#,JIS2000# (FEPA Standard) F240 F280 F320 F360 F400 F500 F600 F800 |
|
Color |
Gray |
Business Nature
Manufacturer
Country/Region
Zhengzhou, China
Main Products
Abrasive Raw Material...
Zhengzhou haixu abrasives co., Ltd, founded in 1 9 9 9, located in Xingyang City, Henan Province, China. With 20 years production experience and professional technical and marketing team, Haixu Abrasives has established long term cooperation with foreign customers which are from about forty countries including United States, Germany, Italy, Japan, Korea, Russia , Malaysia and Vietnam. Zhengzhou Haixu Abrasives Co., Ltd has over 7500 square kilometers workshop for production and QC department with all kinds of testing equipments including Omec, Slap-seive and microscope , Office for accounting, purchasing, importing, exporting, afer-sales service, logistics. HAIXU now become a leading brand in the abrasives material field. Zhengzhou Haixu Abrasives Co., Ltd owns plants of white fused alumina, brown fused alumina, blue fired calcined brown fused alumina, pink fused alumina, silicon carbide, glass beads, used for refractory , blasting, grinding and polishing. Garnet sand for sandblasting and waterjet cutting. Our new plant producing chromite sand is founded in 2016, It is used for foundry, which is original from south africa(We import crushing chrome ore from south africa), and then wash, dry, dust cleaning, sieve, pack in China port, then export to all over the world directly. All the above materials are produced under professional stardard, running under the production standards of GB, FEPA, JIS and AFS seperatly. All staff from Haixu Abrasives are always provide good quality products, professional service and proper solution for all clients all over the world.